Abstract The physical and chemical protection of steel reinforcement afforded by the cover is a consequence of the quality of the concrete and its thickness, with a long-term impact on durability and service life. This study proposed variations in cover based on environmental aggressivity class (EAC) of exposure considering concretes of prescribed compressive strength classes (C20/C25/C30/C40). To this end, concrete mixtures were subjected to accelerated testing in salt spray chambers or carbonation. Accelerated testing was kept for periods long enough to reach each EAC cover level. Thus, the effect of each EAC, from mild to severe, was determined on the physical and mechanical characteristics of each mixture. It was determined that the required reinforcement cover varied linearly with compressive strength. This denoted the possibility of using more than one class of concrete and cover for each EAC. It should be noted that the difference in required cover became greater when using concrete with a strength class higher than C30. Still, it was noticed that the chloride ions attack s was more severe than carbonation and was, for most of the test cases, the determinant factor in minimum cover thickness to ensure the desired durability. longterm term life (EAC C20/C25/C30/C40. C20C25C30C40 CCCC C20/C25/C30/C40 . C20 C25 C30 C40 C (C20/C25/C30/C40) end level Thus mixture Still cases C20C25C30C4 C20/C25/C30/C4 C2 C3 C4 (C20/C25/C30/C40 C20C25C30C C20/C25/C30/C (C20/C25/C30/C4 (C20/C25/C30/C

Resumo O cobrimento das armaduras tem a função de proteger física e quimicamente as armaduras de aço, através da qualidade do concreto e sua espessura, influenciando na durabilidade e vida útil. Este trabalho propôs variações do cobrimento baseados na classe de agressividade ambiental (CAA) de exposição dos concretos, considerando a resistência especificada em cada classe. Os traços foram submetidos aos ensaios acelerados de névoa salina e de carbonatação. Os testes foram mantidos por períodos até que o cobrimento de cada CAA fosse atingido, determinando o impacto no cobrimento das armaduras para cada CAA, mais amena ou mais severa. Cada um destes traços foi avaliado quanto às características físicas e mecânicas. Verificou-se que o cobrimento necessário às armaduras varia de maneira linear com a resistência à compressão dos traços, denotando a possibilidade de considerar mais de uma classe de resistência de concreto e o cobrimento nas diferentes CAA. Destaca-se que a diferença do cobrimento necessário em relação às CAA se torna maior quando utilizados concretos de classe superior a C30. Ainda, percebeu-se que o ataque por íons cloreto é mais severo que a carbonatação, tendo determinado, na maioria das verificações, a espessura mínima de concreto para garantir a durabilidade almejada. aço útil (CAA carbonatação atingido severa mecânicas Verificouse Verificou Destacase Destaca C30 C Ainda percebeuse percebeu determinado verificações almejada C3

ABSTRACT The use of polymeric compounds is limited to sealing masonry in Brazil, due to the criteria of the NBR 16590 [1]. However, one must evaluate how much this material can contribute when applied to structural masonry. Thus, this study investigated the operation of a type of polymeric compound when applied in structural masonry, performing chemical and physical characterization tests and adhesion at the interface between block and binder. Besides these, we investigated the axial compressive strength of full-scale walls was investigated. One sample was made with horizontal joints filled with cementitious mortar and two containing polymeric compound, with 2 and 4 fillets for settlement the blocks. The characterization results of the binder material and interface showed that the polymeric compound has greater resilience and better adherence performance when compared to cementitious mortar. In the overall analysis of the system, it was found that masonry built with 4 fillets of polymeric composite achieved the same compressive strength of the sample built with conventional cement mortar (~ 138 kN/m at break), the sample with 2 fillets presented higher vertical deformation, 25% in relation to the others, showing the potential use of the polymeric compound in structural masonry. Brazil 1659 1. 1 . [1] However Thus these fullscale full scale blocks system ~ ( 13 kNm kN m break, break , break) deformation 25 others 165 [1 16 [

RESUMO O uso dos compostos poliméricos se limita às alvenarias de vedação no Brasil, devido aos critérios da NBR 16590 [1]. No entanto, deve-se avaliar o quanto este material pode contribuir quando aplicado em alvenarias estruturais. Sendo assim, esse estudo investigou o funcionamento de um tipo de composto polimérico, quando aplicado em alvenarias estruturais, realizando ensaios de caracterização química e física do material e de aderência na interface entre bloco e o ligante. Além dessas, foram investigadas a resistência à compressão axial de paredes em escala real, sendo uma amostra executada com as juntas horizontais preenchidas por argamassa cimentícia e outras duas contendo composto polimérico, com 2 e 4 filetes para assentamento dos blocos. Os resultados de caracterização do material ligante e interface mostraram que o composto polimérico possui maior resiliência e melhor desempenho à aderência, quando comparado à argamassa cimentícia. Já na análise global do sistema, verificou-se que a alvenaria construída com 4 filetes de composto polimérico atingiu a mesma resistência à compressão da amostra construída com argamassa cimentícia convencional (~138 kN/m na ruptura), a amostra com 2 filetes apresentou maior deformação vertical, 25 % em relação as demais, mostrando o potencial de utilização do composto polimérico em alvenaria estrutural. Brasil 1659 1. 1 . [1] entanto devese deve estruturais assim dessas real blocos sistema verificouse verificou ~138 138 (~13 kNm kN m ruptura, ruptura , ruptura) vertical demais estrutural 165 [1 ~13 13 (~1 16 [ ~1 (~ ~ (

ABSTRACT The physical and mechanical properties of ceramic blocks are affected by the firing process of the primary raw material, in this case, clay or clay minerals. Consequently, this study sought to characterize different types of silty clays for ceramic block production and determine the effect of firing time and mineral content on their mechanical and physical properties. Characterization was conducted in two stages: pre and post-firing. Pre-firing evaluations were granulometric distribution, Attenberg limits, chemical composition, mineral composition and thermal behavior. Post-firing evaluation made use of 30 specimens subjected to temperatures of 800 °C, 900 °C and 1,000 °C. Results showed that firing temperatures greatly affected mechanical properties. Higher burn temperatures increased tensile strength and reduced water absorption while causing linear shrinkage. This increase in shrinkage raised the possibility of damage to the ceramic material and reduction of overall quality. case minerals Consequently stages postfiring. postfiring post firing. post-firing Prefiring Pre distribution limits behavior Postfiring Post 3 80 C 90 1000 1 000 1,00 quality 8 9 100 00 1,0 10 0 1,

ABSTRACT This paper verified the structural behavior of three configurations of composite beams of wood and steel profiles, analytically by the mixed section homogenization method (MHSM), by experimental tests and simulated by the finite element method (FEM). Unreinforced wooden beam (V-SR), with bent steel sheet profiles fixed with stud (V-PRI) and self-tapping (V-AUT) screws were analyzed. The flexural behavior was analyzed by 3 points of these elements, represented by the load and displacement. It was found that the beam failure form was the same in all configurations, occurring in the tensioned part, without lateral buckling of the steel profiles or plastic deformation of the screws. It was noted that the insertion of steel profiles caused an increase in the strength of the composite beams, being 100% in the V-PRI sample and 32% in the V-AUT. The FEM simulations showed values closer to the bending behavior of the V-SR and V-PRI beams in the elastic regime (ELS). The experimental results of the V-AUT beams were more compatible with the mixed section homogenization model. MHSM, MHSM , (MHSM) FEM. . (FEM) VSR, VSR V SR (V-SR) VPRI PRI (V-PRI selftapping self tapping VAUT AUT (V-AUT elements displacement part 100 32 VAUT. AUT. ELS. ELS (ELS) model (MHSM (FEM (V-SR 10 (ELS 1

RESUMO Este artigo verificou o comportamento estrutural à flexão de três configurações de vigas mistas de madeira e perfis de aço, por meio do método de homogeneização da seção mista, ensaios experimentais e simulação computacional. Foram analisadas viga de madeira sem reforço (V-SR), com perfis de chapa de aço dobrada fixada com parafuso tipo prisioneiro (V-PRI) e autoatarraxante (V-AUT). Foram realizados ensaios de flexão por 3 pontos, obtendo a força de ruptura e deslocamentos. Verificou-se que a forma ruptura das vigas foi similar em todas as configurações, ocorrendo na parte tracionada, sem apresentar flambagem lateral dos perfis de aço ou deformação plástica dos parafusos. Notou-se que a inserção dos perfis de aço ocasionou um aumento na resistência das vigas mistas, sendo de 100% nas vigas com perfis de chapa de aço dobrada fixada com parafuso tipo prisioneiro (V-PRI) e de 32% nas vigas com perfis de chapa de aço dobrada fixada com parafuso tipo autoatarraxante (V-AUT). As simulações pelo método dos elementos finitos apresentaram valores mais próximos ao comportamento na flexão das vigas V-SR e V-PRI no regime elástico (ELS). O método de homogeneização da seção mista mostrou-se mais próximo dos resultados experimentais nas vigas de madeira reforçadas (V-PRI e V-AUT). computacional VSR, VSR V SR , (V-SR) VPRI PRI VAUT. VAUT AUT . (V-AUT) pontos deslocamentos Verificouse Verificou se tracionada parafusos Notouse Notou 100 32 ELS. ELS (ELS) mostrouse mostrou V-AUT) (V-SR (V-AUT 10 (ELS V-AUT 1

resumo: Investigar o comportamento de compósitos cimentícios autocicatrizantes é necessário para conhecer alternativas que possam ser aplicadas em estruturas aumentando a sua vida útil. Portanto, este estudo avaliou a cicatrização do concreto a partir do uso de cápsulas de perlita expandida (PE) e argila expandida (AE) impregnadas com solução de metassilicato de sódio. Esses materiais foram utilizados em substituição aos agregados naturais no concreto nas proporções de 0%, 15% e 30% em relação à massa. Os exemplares foram curados em ambientes úmidos ou submersos. A fissura foi induzida pelo teste de flexão e a cicatrização foi avaliada visualmente e medida por meio de software. Testes de absorção capilar indicaram redução da porosidade das amostras que incorporaram materiais autocurantes, sendo esta uma importante propriedade relacionada à durabilidade do conjunto. As amostras com PE alcançaram 100% de cicatrização com 15% de substituição. O preenchimento da fissura foi obtido em fissuras de até 0,43 mm de largura. Amostras com AE alcançaram 50% de recuperação de fissura sob cura úmida e 90% sob cura submersa. Conclui-se que incorporar a solução de metassilicato de sódio proporcionou melhorias consideráveis na selagem de fissuras e esta solução torna-se uma alternativa eficiente para concretos autocicatrizantes a serem produzidos no Brasil. A incorporação de PE foi mais eficaz do que o AE como material encapsulante. Além disso, o uso de PE não impactou na resistência à compressão em decorrência de sua reduzida dimensão de partícula e empacotamento. Ainda, a EP apresentou maior percentual de cicatrização comparando-se com as amostras contendo AE.

abstract: Investigating the behavior of self-healing cementitious composites is necessary to know alternatives that can be applied in structures increasing their life service. Therefore, this study evaluated concrete self-he aling from the use of expanded perlite (EP) and expanded clay (EC) capsules impregnated with a sodium metasilicate solution. These materials were used to substitute natural aggregates in concrete in proportions of 0 wt·%, 15 wt·% and 30 wt·% which were cured in humid or submerged environments. Cracking was induced with a flexural test and a closing with cicatrization product. was evaluated and measured visually with a software. Capillary absorption tests indicated a reduction in the porosity of samples which incorporated self-healing materials, considering it as an important property related to durability. Samples with EP achieved 100% self-healing with 15% substitution. Crack filling was achieved in cracks up to 0.43 mm wide. Samples with EC achieved 50% crack recovery under humid curing and 90% under submerged curing. It was concluded that incorporating the sodium silicate allowed improvements to fissure sealing and it is an alternative to produce self-healing concrete in Brazil. EP was more effective than EC as encapsulating material. Despite that, the EP did not impact the compressive strength due to its small size and better packing of the mixture, Also, EP presented higher healing percentage when comparing with samples containing EC.

RESUMO Entende-se que as lajes pré-fabricadas mistas são sistemas compostos, nos quais se constituem por vigotas de concreto (armado ou protendido), elementos de preenchimento e uma camada de solidarização em concreto armado. É um sistema construtivo muito utilizado no mundo, principalmente, em países ibero-americanos, como o Brasil e Espanha, por exemplo. No entanto, ainda há desconhecimento sobre a compatibilidade entre os resultados teóricos para os experimentais, uma vez que são sistemas compostos e as variáveis podem ser determinantes nos modelos de previsão. Portanto, este estudo teve como objetivo comparar os resultados teóricos e experimentais de lajes mistas pré-fabricadas. Para isso, desenvolveu um programa experimental de ensaios de flexão para uma laje com vigota central protendida reforçada de cada lado com elementos de laje e uma cobertura de concreto armado com malha de 5 cm. As variáveis experimentais foram o diâmetro da armadura de aço e do material de enchimento (telhas de cerâmica ou blocos de poliestireno expandido). Este estudo tem 4 etapas: caracterização dos materiais, ensaios mecânicos da vigota, efeito do material de enchimento no comportamento estrutural e comportamento teórico e experimental do sistema na fissuração e ruptura. Vigotas protendidas romperam na região de compressão durante os testes de flexão, independentemente do diâmetro da armadura de aço. O material de enchimento não alterou a carga de ruptura das lajes, mas os blocos de EPS permitiram deflexões consideráveis. Em relação ao momento fletor máximo, os modelos teóricos selecionados apresentaram concordância de até 99% nos valores experimentais para vigotas reforçadas com aço de 4 mm de diâmetro. Entretanto, para as nervuras com fios de 5 e 6 mm, a análise não se mostrou tão válida, chegando a uma relação de aproximadamente, 70 e 60%, respectivamente.

ABSTRACT The composite precast slabs are composite systems, in which they are constituted by concrete joists (reinforced or prestressed), filling components and a solidarization layer in reinforced concrete. It is a construction system widely used in the world, mainly in Ibero-American countries, such as Brazil and Spain, for example. However, there is still a lack of knowledge about the compatibility between the theoretical results and the experimental ones, since they are composite systems, and the variables can be decisive in the theoretical models. Therefore, this study aimed to compare the theoretical and experimental results of precast composite slabs. This study developed an experimental program of flexing tests for a slab with pre-stressed center joist reinforced on each side with half-longitudinal slab components and a 5 cm mesh-reinforced concrete cover. Experimental variables were the diameter of steel reinforcement and filler material (ceramic blocks or Expanded Polystyrene – EPS blocks). This study has 4 steps: materials characterization, mechanical tests of the joist, effect of filler material in the structural behavior and theoretical and experimental system behavior at fissuring and rupturing. Prestressed joists ruptured in compression regions during bending tests regardless of the diameter of steel reinforcement due to concrete low strength. Filler material did not alter the slabs rupturing load, but EPS blocks allowed considerable deflections. Regarding maximum bending moment, the selected theoretical models had an agreement of up to 99% on experimental values for 4 mm diameter steel-reinforced joists. However, for the joints with 5 and 6 mm wires, the analysis did not prove to be so valid, reaching a ratio of approximately 70 and 60%, respectively.

Resumo O principal sistema de uma construção é a estrutura. A sua substituição é muitas vezes inviável e a sua reparação ou demolição gera resíduos muitas vezes de difícil reciclagem, reutilização ou descarte. Dessa forma, estruturas com maior vida útil do projeto (VUP) gerarão menores impactos ambientais, além de serem financeiramente mais interessantes para seus usuários. O concreto armado é um dos tipos de estrutura mais utilizados, e comumente sofre com ataques de íons cloreto e carbonatação que podem facilitar a corrosão da armadura. As estruturas de concreto também sofrem efeitos com a passagem do tempo, como aumento da probabilidade de carga acidental, fluência e retração. Este trabalho tem como objetivo propor parâmetros para vidas úteis de projeto superiores a 50 anos, relativos à durabilidade e ao efeito do tempo. O estudo da durabilidade foi conduzido a partir de uma revisão bibliográfica e escolha de modelos de previsão de vida útil baseados em formas características de agressividade ambiental e comparação com normas internacionais, com VUPs entre 50 e 100 anos e utilizando os seguintes parâmetros: relação a/c, resistência à compressão, consumo mínimo de cimento e cobrimento mínimo. O estudo do efeito do tempo considerou as normas brasileiras e sua probabilidade para cargas acidentais, fluência, retração e variações da resistência à compressão, utilizando VUPs entre 50 e 100 anos. Os resultados de durabilidade foram compilados em uma tabela com parâmetros dimensionais práticos recomendados. Apesar de alguns parâmetros propostos serem superiores ou inferiores aos valores de normas, as diferenças de desempenho foram contabilizadas através de outros parâmetros para manter os níveis de segurança e obter espessuras de cobertura mínimas. As cargas verticais variáveis apresentaram incrementos de 4,29% para 75 anos e 7,22% para 100 anos e a velocidade do vento demonstrou uma variação de 5,08% de aumento aos 75 anos e 9,84% aos 100 anos. A resistência à compressão do concreto, o coeficiente de fluência e a deformação específica de retração não apresentaram variações significativas. FBM: conceituação, análise formal, metodologia, redação; BFT e FLB: curadoria de dados, análise formal.

Abstract The main system of a construction is the structure. Its replacement is most of the times unfeasible and its repair or demolition generates waste that is often difficult to recycle, reuse or dispose of. In this way, structures with longer design service life (DSL) will generate lower environmental impacts, in addition to being financially more interesting for their users. Reinforced concrete is one of the most used types of structure, and commonly suffers with attacks of chloride ions and carbon dioxide that can facilitate the corrosion of the reinforcement. Concrete structures also suffer effects from the passage of time, as probability of accidental load increase, creep and shrinkage. The objective of this study was to determine durability and time effect parameters for DSLs between 50 and 100 years. The durability study was conducted through a review of reference studies, a selection of DSL models based on characteristic forms of environmental aggressiveness and comparison with international standards, using DSLs between 50 and 100 years and the following parameters: w/c ratio, compression strength, minimum cement usage and minimum cover. The time effect study considered Brazilian standards and their probability for accidental loads, creep, shrinkage and variations of the compressive strength, using DSLs between 50 and 100 years. The durability results were compiled in a table with practical recommended dimensional parameters. Despite some proposed parameters being higher or lower than standard values, the differences in performance were accounted through other parameters in order to maintain safety levels and to obtain minimum cover thicknesses. Variable vertical loads presented increments of 4.29% for 75 years and 7.22% for 100 years and wind velocity demonstrated a variation of 5.08% increase at 75 years and 9.84% at 100 years. Compression strength of concrete, creep coefficient and specific shrinkage deformation did not present significant variations. FBM: conceptualization, formal analysis, methodology, writing; BFT e FLB: data curation, formal analysis.

Resumo Soluções bacterianas têm sido estudadas para promover a autocura de matrizes cimentícias, entretanto, a concentração dessas soluções variou entre os estudos. Consequentemente, o objetivo deste estudo foi avaliar o potencial de autocura de diferentes concentrações de Bacillus subtilis AP91 encapsulado em perlita expandida (PE). O exame visual e a absorção capilar de água foram medidos ao longo do tempo. As amostras de teste também foram submetidas a testes de resistência de força. Foram avaliadas as propriedades físico-químicas do EP e sua distribuição na matriz. Não houve tendência observada no efeito da concentração da solução na largura da fissura cicatrizada. No entanto, a concentração afetou a quantidade e o comprimento das fissuras cicatrizadas. A absorção capilar diminuiu conforme as fissuras foram curadas, enquanto nenhuma mudança significativa foi medida na resistência da força, independentemente da concentração. Os resultados indicaram que a EP proporcionou encapsulamento adequado à solução bacteriana e que há uma distribuição adequada das cápsulas na matriz cimentícia.

Abstract Bacterial solutions have been studied to promote self-healing of cementitious matrices, however, the concentration of this solutions varied between studies. Consequently, the objective of this study was to evaluate the self-healing potential of different concentrations of Bacillus subtilis AP91 encapsulated in expanded perlite (EP). Visual examination and capillary absorption of water was measured over time. Test samples were also subjected to strength resistance tests. The physiochemical properties of EP and his distribution on the matrix was evaluated. There was no observable trend in the effect of solution concentration on the width of crack healed. However, concentration affected the quantity and length of the fissures healed. Capillary absorption decreased as fissures were healed while no significant changes were measured in strength resistance regardless of the concentration. Results indicated that EP provided suitable encapsulation to the bacterial solution and there is an adequate distribution of the capsules in the cementitious matrix.

RESUMO Durante um incêndio, a alvenaria pode se degradar devido a ação das altas temperaturas. O revestimento de argamassa, sendo o último componente da alvenaria, pode sofrer uma redução considerável em suas propriedades mecânicas. O estudo de alterações macroestruturais, como a resistência de aderência à tração em argamassas de revestimento diante da exposição da alvenaria a altas temperaturas, é importante para compreender o nível de degradação das paredes de alvenaria para que se possa aperfeiçoar as recomendações de projeto e garantir a segurança dos usuários durante uma situação de incêndio. Neste sentido, esta investigação busca analisar a resistência de aderência à tração do revestimento de argamassa em paredes de alvenaria, em condições de temperatura ambiente e em altas temperaturas. O programa experimental consistiu em confeccionar uma parede de alvenaria em escala real e submetê-la à curva padrão ISO 834 durante 240 minutos. Antes do programa térmico iniciar, foram realizados os ensaios de resistência à tração do revestimento de argamassa nas extremidades da parede, região que não é afetada pela ação térmica. Após o ensaio de resistência ao fogo foi verificada a resistência de aderência à tração na superfície não exposta e os resultados foram submetidos a uma análise estatística. Apesar da alvenaria ter mantido sua estabilidade e estanqueidade durante os 240 minutos do ensaio de resistência ao fogo, foi classificada como EI-180, visto que a capacidade de isolamento térmico se manteve por 193 minutos. Observou-se uma redução de 71,4% na resistência de aderência do revestimento de argamassa com o substrato após a exposição da parede às altas temperaturas, indicando uma variância estatisticamente significativa.

ABSTRACT During a fire, the masonry can degrade due to the action of high temperatures. Mortar coating, being the last component of masonry, can suffer a considerable reduction in its mechanical properties. The study of macro-structural changes, such as the tensile bond strength in coating mortars when masonry is exposed to high temperatures is important to understand the level of degradation of masonry walls to allow the improvement of the design recommendations and ensure the user safety during a fire situation. In this sense, this investigation seeks to analyze the tensile bond strength of the mortar coating on masonry walls at ambient temperature and high temperature. For the experimental study, a full-scale masonry wall was built and submitted to the ISO 834 standard curve for 240 minutes. Before the thermal program starts, the tensile bond strength tests of the mortar coating were carried out at the ends of the wall which is a region that is not affected by the thermal action. After the fire resistance test, the tensile bond strength on the unexposed surface was verified and the results were subjected to statistical analysis. Although the wall maintained its stability and integrity during the 240 minutes of the fire resistance test, it was classified as EI-180, since the thermal insulation capacity was maintained for 190 minutes. A reduction of 71.4% in the tensile bond strength of the mortar coating with the substrate was observed after the exposure of the wall to high temperatures, indicating that the variance is statistically significant.

Resumo Considerando o uso expressivo no cenário nacional de lajes pré-fabricadas de concreto com elementos inertes de preenchimento do tipo cerâmico, este trabalho contém a avaliação do comportamento do sistema frente a ruídos aéreos e de impacto, em diferentes composições. Foram realizados ensaios em câmara reverberante vertical, conforme a ISO 10140-5:2010. As variações empregadas nos sistemas foram contrapiso, camada resiliente, revestimentos de laminado de madeira e porcelanato, reboco de argamassa e forro suspenso. Os resultados evidenciaram que o desempenho acústico ao som de impacto da laje pré-fabricada de concreto com lajota cerâmica é afetado pelo efeito da ressonância nas cavidades das lajotas e que a adição de contrapiso pode compensar o menor isolamento acústico em comparação à laje de concreto maciço, em razão do consequente aumento na massa do sistema. Os resultados também mostraram que, para o isolamento ao ruído aéreo, não existem diferenças significativas entre os revestimentos de porcelanato e piso laminado e que a instalação do forro compensou a reduzida perda de transmissão sonora da laje vigota/lajota em relação à laje de concreto maciço.

Abstract Considering the widespread use of T-beam/hollow-block slabs in Brazil, this study examines the behaviour of that system under the effect of airborne and impact noises, in different compositions. Tests were carried out at a specific test facility, according to ISO 10140-5: 2010. The variations used in the systems were: subfloor, resilient layer, wood laminate and porcelain tile floorings, mortar plaster and suspended ceilings. The results showed that the acoustic performance of the T-beam/hollow-block slab is affected by the effect of resonance in the blocks’ cavities and that the addition of a subfloor can compensate the acoustic fragility when compared with the concrete slab, because of the consequent increase in the system’s mass. The results also show that, for the airborne sound insulation, there are no significant differences between the porcelain tiles and the wood laminate flooring, and that the installation of the suspended ceiling made up for the small sound transmission loss of the T-beam/hollow-block slab in relation to the concrete slab.

Resumo Os materiais que compõem um sistema construtivo influenciam diretamente no desempenho acústico de edificações. Em sistemas de alvenaria, por meio de experimentos, a geometria dos blocos e os tipos de revestimento foram elencados como os fatores fundamentais no desempenho acústico de paredes. Portanto, este estudo tem o objetivo de enriquecer tal base de dados e promover análises para a indústria da construção civil por meio da avaliação da redução aos sons aéreos de paredes de alvenaria em blocos cerâmicos com e sem a aplicação de revestimento em argamassa. Para tal, diferentes sistemas de parede, compostos por blocos cerâmicos distintos, foram construídos para a determinação das diferenças de desempenho e comportamento dos sistemas devido às suas características físicas e a influência do revestimento em argamassa. Estas análises foram feitas em ambiente laboratorial. Como resultado, sem o revestimento, a maior redução sonora foi obtida nas amostras com maior massa superficial e maior relação A liq /A t (relação entre a área líquida e bruta dos blocos cerâmicos). Com o revestimento em argamassa a redução sonora foi aumentada. Neste caso, a massa superficial foi a característica mais influente, em comparação à relação A liq /A t , apesar de que os melhores resultados foram encontrados em amostras de maior relação A liq /A t .

Abstract The materials that compose a construction system influence directly the acoustic performance of buildings.In masonry systems, through experiments, the geometry of the blocks and the types of coating were perceived as fundamental factors on the acoustic performance of walls. Therefore, this study intends to enrich the database and promote analysis for the civil construction industry by evaluating the airborne sound reduction of masonry walls composed by ceramic blocks with and without mortar coating. Accordingly, different partitions made of different ceramic blocks were built to determine the performance discrepancies in the partitions’ behavior due to physical characteristics and the influence of the mortar coating. These analyses were made in laboratory. As a result, without coating, the highest sound reduction was observed in the samples with more bulk mass and higher Aliq/At ratio (relationship between the net and gross areas of the ceramic blocks). Then, with the mortar coating, the coating improved the sound reduction. Moreover, the bulk mass was the most influential characteristic in comparison to the Aliq/At ratio, even though the best results were obtained in the samples with higher Aliq/At ratios.

Resumo Neste artigo, foi avaliada experimentalmente a influência do diâmetro de barras no grau de redução da resistência ao escoamento (fy) e de ruptura (fu) de armaduras extraídas de quatro pilares expostos à ação térmica em um forno vertical, pela curva padrão de aquecimento da ISO 834-1:1999, por 240 min. Os pilares tinham seção transversal de 25 cm x 25 cm e altura de 300 cm. Os diâmetros analisados foram de 10 mm e 16 mm, e a espessura de cobrimento, de 25 mm a 50 mm. Os resultados mostraram que, independentemente da espessura de cobrimento, as barras com 16 mm de diâmetro sofreram maior redução na resistência de escoamento (fy) e na resistência última (fu) em relação às barras de 10 mm de diâmetro, devido ao maior volume de desplacamento do concreto dos pilares, com exposição direta às temperaturas elevadas. Os maiores volumes de desplacamento foram identificados nos elementos com maior espessura de cobrimento (50 mm), atingindo valores até 52 vezes maiores que os desplacamentos identificados nos elementos com espessura de 25 mm no cobrimento. As tensões fy das armaduras obtiveram redução entre 29% e 56%. Assim, com base neste estudo, mostra-se relevante prever a redução do fy e do fu das armaduras no dimensionamento das estruturas de concreto armado em situação de incêndio.

Abstract This paper presents results obtained in tensile tests performed in steel reinforcing bars with different diameters extracted from columns exposed for 240 minutes to the standard fire curve prescribed by ISO 834-1:1999. The square columns were 300 cm long and had a width of 25 mm. The longitudinal reinforcement consisted of 10 mm and 16 mm-diameter steel bars with a concrete cover thickness of 25, 30, 40, and 50 mm. Results showed that 16 mm-diameter bars presented lower yield (fy) and ultimate (fu) stress due to the larger spalled areas of concrete in those columns, which increased its exposure to elevated temperatures. Columns with higher concrete cover thickness (50 mm) presented larger volume of concrete spalling and were accounted to be 52 times higher than elements with cover thickness of 25 mm. It was verified that the residual yield stress was 29-56% lower than the original yield strength, highlighting the the need of a proper post-fire assessment of this type of structure after exposure to fire.

Resumo A busca pela redução do consumo de cimento em compósitos cimentícios se mostra uma preocupação mundial, e a substituição parcial do cimento por resíduos industriais tem ganhado impulsão. Um desses materiais é o vidro, material rico em sílica amorfa, mas que pode apresentar problemas em sua utilização, devido à reação álcali sílica (RAS). O objetivo da pesquisa foi analisar as resistências à compressão de argamassas com uso de resíduo moído de vidro (RMV). Foram testados dois tempos de moagem para RMV, 16 e 32 horas, bem como percentuais de 10, 15 e 20% de substituição em massa de cimento por RMV. Uma análise estatística foi realizada para verificar quais fatores interferiam na resistência das argamassas. O efeito mitigador do RMV também foi testado quanto à RAS. Os resultados mostraram que o tempo de moagem não foi significativo para resistência, mas os percentuais de substituição foram. O percentual de 20% mostrou-se o melhor, uma vez que foi estatisticamente igual ao traço padrão.

Abstract The necessity to reduce the consumption of cement in cementitious composites is a worldwide concern and the partial replacement of cement with industrial waste has gathered considerable interest. One type of industrial waste is glass, which is rich in amorphous silica but can present problems with its use due to the alkali-silica reaction (ASR). The objective of this study was to analyze the compressive strengths of mortars using ground glass residue (GLR). Milling times of 16 h and 32 h were conducted and GLR tested in cement substitutions of 10 w.t.%, 15 w.t.% and 20 w.t.%. A statistical analysis was performed to verify which factors affected mortar strength. The mitigating effect of GLR in ASR was also tested. Results showed that milling time did not affect resistance significantly but w.t.% substitution did. The substitution of 20 w.t.% proved to provide the best result as it was statistically equal to the standard mixture.

RESUMO Diante da incorporação de resíduos no concreto, ocorre uma diminuição do impacto ambiental das edificações. Um dos objetivos do desenvolvimento atual é o emprego de fontes de energia de baixo impacto, como a cinzas pesadas de carvão (coal bottom ash, CBA) (15% resíduos totais), que possuem densidade superior às cinzas volantes e se acumulam nos silos. Diante desse cenário, o presente trabalho avaliou a viabilidade de incorporação da CBA na composição do concreto celular, em substituição à sílica ativa. Este estudo compreendeu a caracterização e aplicação da CBA. Para tal, foi realizada microscopia eletrônico de varredura (MEV) associado à análise de energia dispersiva (EDS), granulometria a laser, difração de raios X (DRX), eflorescência de raios X e densidade. Após a incorporação dos resíduos no concreto celular substituindo a sílica ativa, foi realizada análise de resistência à compressão e novamente MEV, avaliando o impacto da inserção da CBA na microestrutura do concreto. Os resultados de XRD são complementares às outras análises. Com a técnica SEM, observou-se a predominância de partículas com formato esférico. A resistência à compressão dos concretos CBA foi superior ao concreto de referência variando de 0,13 a 0,74MPa.

ABSTRACT Ahead of the incorporation of residues in concrete composition, there is a decline in the environmental impact of buildings. One of the goals of today’s development is the employment of low-impact energy sources, such as thermoelectric. Thermoelectric industries display a high rate of residues, among which is pointed out coal bottom ash (CBA) (15% total residues), which have density superior to fly ash and accumulates in silos. Considering this scenario, this paper assessed the incorporation feasibility of CBA in the composition of cellular concrete, replacing silica fume. This study comprehended CBA characterization and application. For such, it was performed a scanning electron microscope (SEM) associated with Energy dispersive spectroscopy (EDS) analysis, laser granulometry, X-ray diffraction (XRD), X-ray efflorescence and density. Following the incorporation of the residues in cellular concrete in place of silica fume, it was performed compression strength analysis and SEM anew, evaluating the impact of CBA’s insertion in concrete’s microstructure. The XRD results are complementary to the other analyses. With SEM technique, it was observed the predominance of spherical-shape particles. The compressive strength of CBA concretes was superior to the reference concrete from 0,13 to 0,74MPa.

RESUMO O método da maturidade é um procedimento que associa a evolução da temperatura do concreto e o avanço de suas propriedades no estado endurecido, como a resistência à compressão, geralmente em idades iniciais. Sua aplicação é justificada quando se requer segurança e agilidade para tarefas de construção, como a protensão, a remoção do escoramento, o desmolde e a cura de concreto em baixas temperaturas. As regiões de clima temperado são conhecidas por apresentar temperaturas mais baixas durante o inverno, o que pode retardar o ganho de resistência do concreto. Este estudo aplicou o método de maturidade em uma estrutura de concreto armado localizada no Sul do Brasil, em uma construção industrial. Se observou que o concreto, do qual se esperava o alcance de 30 MPa aos 28 dias, chegou a alcançar 70% da resistência com 8,5 dias para a laje 1 e em 4,4 dias para a laje 2, sendo possível mensurar tal propriedade utilizando o método da maturidade.

ABSTRACT The maturity method is a procedure that associates the evolution of the temperature of concrete cast to the structure and the evolution of its hardened state properties like compressive strength, usually at early ages. Its use is justified when safety and agility are required for activities like prestressing, shoring removal, demolding and low temperature concrete curing analysis. Temperate regions are known for having lower temperatures during the winter, which can delay concrete strength gains. The aim of this study was to apply the maturity method to a reinforced concrete structure located in Southern Brazil in industrial construction. It was noted that the concrete, despite being expected to reach 30 MPa at 28 days, managed to reach 70% of the strength at 8.5 days for slab 1. Slab 2, whose function was to support garners 4, 5 and 6, presented the data at 4.4 days, it being possible to measure such property using the maturity method.